Iranian Journal of Chemical Engineering (IJChE)

Abstract The goal of this study was to examine the morphology and characteristics of a blend of polylactic acid (PLA) with thermoplastic corn starch (TPS) and polyethylene glycol (PEG-400) using the extrusion process. The blends were evaluated through the tensile and impact strength tests, scanning electron microscopy (SEM), and X-ray diffraction (XRD) analysis. The experimental design method was selected to quantitatively analyze the influence of the content of TPS and concentration of the plasticizer on mechanical properties. Results from the tensile test showed that the addition of PEG-400 decreased tensile strength and elastic modulus, but increased elongation at break and impact strength, significantly. The blend with 20% TPS and 20 phr PEG-400 had the best overall performance in terms of tensile strength, elastic modulus, elongation at break, and impact strength. The SEM analysis indicated increased incompatibility and phase separation in samples with 40% TPS. Additionally, at high concentrations of PEG-400, the excessive plasticizer caused polymer saturation, resulting in unabsorbed plasticizer and phase separation. The findings suggest that the blend with 20% TPS and 20 phr PEG-400 could be suitable for use in eco-friendly applications.

Abstract In this study, the main purpose has been to investigate the behavior of the nanoparticles with different structures and similar based materials in polymer nanocomposites. To this end, different samples, containing PS as the matrix, and layered graphene oxide (GO) and/or hollow graphene oxide nanoparticles (HGO), were prepared via the melt mixing process and were subjected to heat conduction and tensile tests. To evaluate all features of the interaction between the polymer phase and the nanoparticles, a thermal/mechanical analytical model was proposed and the results were used to simulate the behavior of specific geometrical structures, corresponding to the real samples, under different thermal/mechanical conditions. The results showed good agreement between the obtained experimental data and simulation/analytical model interpretations. In addition, it was found that the HGO nanoparticle had such a good performance in enhancing the thermal and mechanical properties of the nanocomposite, due to its unique structure.

Abstract This research work focuses on the performance optimization of composites containing both micron and nano size TiO 2 particles separately in various concentrations and to understand the role of each on the thermal stability and moduli of the composites. Thermal stability of the particle-reinforced composites increased on increasing the concentration of TiO 2, both in nano and micron filled cases, except for the 2.5 wt% nano-filled composite. Storage modulus (E') increased on adding micron-TiO2 to the epoxy hardener resin system from 1 - 2.5 - 5 wt% respectively and decreased dramatically on further increasing the micron TiO 2 content to 7.5 and 10 wt% respectively. Nano TiO 2 particle-reinforced composites showed an increasing trend of storage modulus for 2.5 - 5 - 7.5 wt% TiO 2 filled composites with respect to the neat
resin system. Presence of both micron and nano TiO2 particles increased the T g of the composites. Also, the effect of sonication on the modulus and Tg is discussed. As a whole, composites in which the TiO 2 particles were dispersed through the resin matrix by glass rod revealed better results (higher storage moduli and T g) than those mixed by sonication, due to high viscosity of the epoxy resin used.

Abstract The effect of cobalt naphthenate and 2-benzoylbenzoic acid on UV-photooxidative degradation of low density polyethylene have been studied. Sheets of these samples were prepared from polyethylene and different concentrations of cobalt naphthenate and 2-benzoylbenzoic acid then these samples were UV-irradiated. Changes in the carbonyl index, tensile strength, elongation at break, crystallinity and density were measured to monitor the degradation. The measurements were done before and after UV-irradiation at every 30-day interval for 90 days. The results show that the UV-irradiation affects the rate of degradation of LDPE with increasing the concentration of the cobalt naphthenate and 2-benzoylbenzoic acid. The increasing rate of degradation is more obvious for the increased concentration of cobalt naphthenate and also the time of irradiation, but the rate of degradation is decreased by incorporation of 2-benzoylbenzoic acid.

Abstract The effect of cobalt naphthenate and 2-benzoylbenzoic acid on UV-photooxidative degradation of low density polyethylene have been studied. Sheets of these samples were prepared from polyethylene and different concentrations of cobalt naphthenate and 2-benzoylbenzoic acid then these samples were UV-irradiated. Changes in the carbonyl index, tensile strength, elongation at break, crystallinity and density were measured to monitor the degradation. The measurements were done before and after UV-irradiation at every 30-day interval for 90 days. The results show that the UV-irradiation affects the rate of degradation of LDPE with increasing the concentration of the cobalt naphthenate and 2-benzoylbenzoic acid. The increasing rate of degradation is more obvious for the increased concentration of cobalt naphthenate and also the time of irradiation, but the rate of degradation is decreased by incorporation of 2-benzoylbenzoic acid.